流化床锅炉、垃圾焚烧炉用耐磨衬里浇注料
Wearable materials for CFB boilers and garbage furnace's lining
项目 Ptoperites |
指标 Specification |
| 牌号 Brands |
|
自流式刚玉浇注料 self-flowing corundum castables YG-GL-14 |
刚玉质耐磨可塑料 corundum wearable plastic refractory YG-ZGS-13 |
轻质保温浇注料 light weightinsulating castables YG-LG-08 |
中质保温浇注料 middle weight insulating castables YG-ZJ-16 |
粘结胶泥 bonding slurries YG-GMN-13 |
耐火度 CCS,MPa |
＞1790 |
＞1790 |
＞1200 |
＞1500 |
＞1700 |
体积密度,BD,g/cm3 |
2.9 |
2.8 |
0.8 |
＜1.6 |
2.1 |
耐压强度
CCS,Mpa |
110℃×24h |
110-120 |
＞70 |
3 |
＞12.5 |
粘结强度 4.5Mpa cohering strength |
1100℃×3h |
120-130 |
＞85 |
5.5 |
＞16 |
1380℃烘干 |
／ |
110-120 |
／ |
／ |
抗折强度
MOR,Mpa |
110℃烘干 |
＞8 |
＞7 |
／ |
／ |
／ |
1100℃烘后 |
＞13 |
＞10 |
／ |
／ |
／ |
1350℃烘后 |
＞10 |
＞8 |
／ |
／ |
／ |
重烧线变化率
Linear change on reheating,( 1100℃×3h),% |
0.1 |
0.2 |
＜0.3 |
0.2 |
／ |
热震稳定性，次
Thermal shock resistance,cycles |
＞20 |
＞40 |
／ |
＞20 |
／ |
最高工作温度
Maximum service temperature,℃ |
1650 |
1450 |
1250 |
1350 |
|
导热系数 Thermal conductivity,W/(m·k) |
／ |
／ |
0.35 |
0.45 |
／ |
耐磨性 Abrasion resistance,C.C |
6.5 |
＜8 |
／ |
／ |
／ |
普通耐火浇注料
Ordinary refractory castables
本产品是以粘土和高铝质原料为骨料和粉料，加结合剂制成的耐火浇注料。主要用于各种工业窑炉等热工设备内衬及化工行业各种窑炉。产品具有较高的耐火性能、良好的热震稳定性，并具有一定的抗硫酸盐侵蚀性能。其使用温度一般在 1350-1400℃，如要提高使用温度，可采用氧化铝水泥及调整颗粒级配。产品还具有抗菌素酸性、碱性良好性能，而且强度高，烧后无裂缝剥落现象。
These products mainly use chamotts and bauxite as aggregate and fine. They have high refractoriness. good sulphate corrosion resistance, Their service temperature is within 1350-1400 ℃, If service temperature is called for higher degree, particle size distribution can be addition usted and binder can be substiute by alumina cemen thus castables have acid-resistance, alkaliresistance, acid-resistance and high strength, spall resistance properties.
|
A608 高铝质
Bauxite castable |
A609 粘土质
Chamotte castable |
化学成份
Chemical Composition,% |
Al2O3 |
≥75 |
≥55 |
Fe2O3 |
≤1.5 |
≤2.0 |
| 耐火度 Refractoriness,℃ |
1770 |
1650 |
| 体积密度，BD，（110℃×24h),g/cm3 |
2.5 |
2.4 |
| 耐压强度 CCS，Mpa |
110℃×24h |
≥45 |
≥35 |
1400℃×3h |
65-88 |
55-60 |
| 抗折强度 MOR,Mpa |
110℃×24h |
≥4.8 |
≥4.5 |
850℃×3h |
≥11.5 |
≥6.5 |
| 荷重软化温度 RUL,℃ |
1450 |
1370 |
| 线变化率 PLC,% |
1350℃×3h |
+0.2 |
+0.18 |
1450℃×3h |
-0.6 |
-0.2 |
热震稳定性，（800℃水冷）,次
Thermal shock resistance (800℃-water quench), cycles |
18 |
18 |
流化床锅炉用系列耐磨浇注料
Wearable Castables for CFB boilers
|
耐磨浇注料
wearable bauxite castable |
高强度刚玉耐磨可塑料
High strength wearable Corundum Plastic refractory |
高强度耐磨浇注料
Brown Corundum wearable castable |
YG-LJ-13 |
YG-GS-13 |
YG-TJ-13 |
Al2O3，% |
75 |
85 |
85 |
| 耐火度 Refractoriness,℃ |
＞1790 |
1780 |
1780 |
| 体积密度，BD,（110℃×24h),g/cm3 |
2.7 |
2.9-3.1 |
3.1 |
| 耐压强度 CCS,Mpa |
110℃×24h |
＞110 |
65 |
≥100 |
1100℃×3h |
125-130 |
80-100 |
120-125 |
1380℃×24h |
— |
≥125 |
— |
| 抗折强度 MOR,Mpa |
110℃×24h |
＞10 |
＞5 |
8 |
1100℃×3h |
＞12 |
＞8 |
12 |
| 线变化率 PLC,(1350℃×3h)% |
-0.14 |
-0.4 |
-0.5 |
热震稳定性，(1100℃水冷),次
Thermal shock resistance(1100℃-water quench),cycles |
＞20 |
＞26 |
25 |
| 最高工作温度 Maximum service temperature,℃ |
1500 |
1550 |
1550 |
| 耐磨性 Abrasion resistance,C.C |
＜10 |
＜8 |
＜6.5 |