中间包镁质干式振动料
性能 |
指标 |
MgO,% |
≥86.5 |
体积密度
g/cm3 |
110℃×24h |
≥2.39 |
1600℃×3h |
≥2.35 |
抗折强度,1600℃×3h Mpa |
≥4 |
线变化率,1600℃×3h |
－1.01 |
镁钙质干式振动料
性能 |
指标 |
MgO,% |
≥76 |
CaO,% |
≥15.5 |
体积密度
g/cm3 |
110℃×24h |
≥2.2 |
1600℃×3h |
≥2.2 |
抗折强度，1600℃×3h Mpa |
≥4.4 |
线变化率,1600℃×3h |
－1.2 |
刚玉制品
Corundum proucts
本产品采用电熔刚玉砂、纯氧化铝细粉为主要原料，经机械成型，高温烧成等工序制成。制品具有耐高温、耐腐蚀、热震稳定性好等特点，适用于石化工业、大中型合成氨气化炉与造气炉及轧钢加热炉底、出钢槽、各种高温电炉、钼钨丝高温炉、陶瓷煅烧炉、氧化铝瓷烧结炉等，也可作高温中的辅助材料，如匣钵、窑车砖等。
With fused white corundum aggregate and a-alumina fine as main raw materials, through mechanical mold and high temperature sintered , these products have high refractoriness . Good corrosion resistance ,antioxidation and thermal shock resistance. They are suitable for petro-chemical industry (like large and medium sized synthetic ammonia vaporization furnace and gasometry ) and metallurgical industry (for example , the bottom of roll steel heating furnace , steel spout , various kinds of high temperature furnace and ceramic sintered furnace) . Also can be used as auxiliary material in high temperature industry like kiln furniture like pusher.
|
GY-85 |
GY-95 |
化学成份 Chemiacl composition |
Al2O3% |
≥85 |
≥95 |
Fe2O3% |
≤0.5 |
≤0.3 |
显气孔率 Apparent porosity,% |
≤21 |
≤20 |
体积密度 BD,g/cm3 |
3.0 |
3.2 |
耐火度℃ Refractoriness, ℃ |
1790 |
1790 |
| 耐压强度 CCS,Mpa |
≥80 |
80-90 |
荷重软化开始温度 RUL,℃ |
≥1530 |
≥1550 |
重烧线变化 % Variation of reburning line （1550℃× 3h） |
0.3 |
0.2 |
喷补(涂)料、涂抹料
产品名称
理化指标
|
镁质喷补涂料 |
高铝质喷补涂料 |
| MgO,% |
≥90 |
— |
| Al2O3,% |
2.5 |
≥65 |
| Fe2O3,% |
— |
≤2.0 |
| 体积密度BD(1200℃烧后),g/cm3 |
≥2 |
2 |
| 耐火度,℃ |
1780 |
1600 |
| 抗折强度Mpa |
110℃烘干(热态) |
≥4
|
≥4 |
| 1200℃烧后 |
0.5 |
— |
| 1400℃烧后 |
— |
≥0.3 |
| 加热线变化，% |
1200℃×3h |
±1.0 |
— |
| 1400℃×3h |
— |
1.0 |
| 最高使用温度,℃ |
1450 |
1400 |
|
以上两种喷补涂料适用于各种窑炉燃烧室、蓄热室、各种热风管道内壁、冶金行业高炉和热风炉，作为补修和保护层之用。
产品名称
理化指标 |
镁质涂料 |
铬镁质涂料 |
刚玉质涂料 |
| MgO,% |
≥90 |
≥65 |
— |
| Al2O3,% |
— |
— |
≥92 |
| Cr2O3,% |
— |
5-8 |
— |
| 体积密度 BD,g/cm3 |
1.8-2.5 |
≥2.4 |
≥2.9 |
| 耐压强度Mpa |
110℃烘干×24h |
≥8
|
≥10 |
40 |
| 1500℃烧后×3h |
＞10 |
＞15 |
≥60 |
涂料在高温工业窑炉中应用很广，用于作保护层，如镁质、铬镁质涂料适用于连铸中间仓；刚玉质涂料适用于石油化工催化、裂化装置，施工简便、灵活，可以捣打，也可涂抹。