铝镁铬系列制品 
ALUINIUM/MAGNESIUM/CHROMIUM SERIES PRODUCTS
公司生产的铝镁铬系列制品广泛应用于有色冶炼、炉外精炼、电炉、转炉等热工窑炉工作内衬、制品不沾渣、耐侵蚀、抗剥落，具有良好的高温性能。
They are widely used in non-ferruous metal smelting,refining smelting,electric fur-nace,converter as inner lining,featuring for non-adhering of salg,antitemperture property.
项目 Item |
品 种 Variety
|
镁铬砖 Magnesium/chromium brick |
铝铬砖 Aluminlum/chromium brick |
镁铝铬砖 Magnesium /aluminium/chromium |
| MgO % |
≥65 |
- |
≥87.5 |
| Al2O3 ％ |
- |
70-80 |
≥5.5 |
| Cr2O3 ％ |
10-25 |
10-20 |
≥1.5 |
| SiO2 ％ |
- |
≤3 |
- |
| 显气孔率 % Rate Gas hole indicating |
≤18 |
≤22 |
5 |
| 体积密度 g/cm3 ≥ Volume density |
≥3 |
|
|
| 常温耐压强度 Mpa Pressure resistance at normal temperature |
≥40 |
＞40 |
≥15 |
| 0.2Mpa 荷重软化温度℃ Softening temperature at the load of 0.2Mpa |
≥1680 |
≥1620 |
≥1650 |
| 重烧线变化 % Variation of re-burning line |
- |
(1600℃×3h)0.5 |
- |
| 抗折强度 Mpa Anti-braking |
1200℃-1480℃ ≥6 |
- |
- |
高强度树脂镁碳砖等级制品各指标  
项 目 |
一级品 |
二级品 |
三级品 |
指 标 |
指 标 |
指 标 |
MT10A |
MT10B |
MT10C |
MT14A |
MT14B |
MT14C |
MT18A |
MT18B |
MT18C |
| Mgo,% 不小于 |
80 |
78 |
76 |
76 |
74 |
74 |
72 |
70 |
70 |
| C,% 不小于 |
10 |
10 |
10 |
14 |
14 |
14 |
18 |
18 |
18 |
| 显气孔率，% 不大于 |
4 |
5 |
6 |
4 |
5 |
6 |
3 |
4 |
5 |
| 体积密度，g/cm3 不小于 |
2.90 |
2.85 |
2.80 |
2.90 |
2.82 |
2.77 |
2.90 |
2.82 |
2.77 |
| 常温耐压强度 不小于 |
40 |
35 |
30 |
40 |
35 |
25 |
40 |
35 |
25 |
| 高温抗折强度，Mpa 1400℃,30min,Mpa 不小于 |
6 |
5 |
4 |
12 |
8 |
5 |
10 |
7 |
4 |
高强度树脂镁碳砖
广泛应用于转炉、电弧炉、大功率直交流电炉渣线、出钢口等部位。